CUPRO-NICKEL ALLOY 706

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: COPPER NICKEL 10%

88.6% CU / 10% NI / 1.4% FE

ASME SPEC NO.: SB171 and 402

SAE ALLOY NO.:

MILITARY SPEC.:MIL-C-15726

ASTM ALLOY NO.:B122

FEDERAL SPECS.:

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.323

MOD. OF ELAST.(x 10****** PSI, tension): 18

ELECT. COND.(% IACS at 68 F (20 C) as annealed): 9

THERM. COND.

(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C): 26

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C): 9.5

CUPRO-NICKEL 706

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 43 - 50

25 max.

1/2 hard: 58 - 72

55 - 71

full hard: 71 - 83

69 - 81

spring: 78 - 88

76 min.

Top of Page

ELONGATION(% in 2 inches(= % in 50mm)

annealed: 33 - 37

1/2 hard: 2 - 9

full hard: 1 - 2

spring: 1 max.

ROCKWELL B HARDNESS
(.020 gauge and over(Rockwell F or 30 T where noted)

annealed: 66 - 84(F)

1/2 hard: 66 - 81

full hard: 76 - 86

spring: 83 - 91

Top of Page

CUPRO-NICKEL ALLOY 715

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: COPPER NICKEL 30% 69.4% CU / 30% NI / 0.6% FE

ASME SPEC NO.: SB171 and 402

SAE ALLOY NO.: MILITARY SPEC.:MIL-C-15726

MILITARY SPEC.:MIL-C-15726

ASTM ALLOY NO.:B122

FEDERAL SPECS.:

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.323

MOD. OF ELAST.(x 10****** PSI, tension):22

ELECT. COND.(% IACS at 68 F (20 C) as annealed):4.6

THERM. COND.

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C):9.0

Top of Page

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 52 MIN.

1/2 hard: 66 - 80

60 - 78

full hard: 75 - 88

73 - 84

spring: 84 - 94

81 -90

ELONGATION
(% in 2 inches(= % in 50mm)

annealed: 30 MIN.

1/2 hard: 3 - 10

full hard: 2 - 4

spring:1 - 2

ROCKWELL B HARDNESS
(.020 gauge and over(Rockwell F or 30 T where noted)

annealed:

1/2 hard: 76 - 85

full hard: 83 - 89

spring: 87- 91

Top of Page

COPPER/NICKEL/TIN ALLOY 725

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: COPPER-NICKEL-TIN ALLOY 88.2% CU / 9.5% NI / 2.3% SN

ASME SPEC NO.:

SAE ALLOY NO.:

MILITARY SPEC.:

ASTM ALLOY NO.:B122

FEDERAL SPECS.:

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.321

MOD. OF ELAST.(x 10****** PSI, tension):20

ELECT. COND.(% IACS at 68 F (20 C) as annealed):11

THERM. COND.

(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C):31

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C):9.2

Top of Page

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 45 - 65

18 - 25

1/2 hard: 65 - 80

59 - 78

full hard: 75 - 90

73 - 88

spring: 85 - 100

83 -97

ELONGATION
(% in 2 inches(= % in 50mm)

annealed: 34 - 36.

1/2 hard: 3 - 17

full hard: 1 - 5

spring:1 - 2

ROCKWELL B HARDNESS
(.020 gauge and over (Rockwell F or 30 T where noted)

annealed: 50 MAX(30t)

1/2 hard: 70 - 90

full hard: 75 -90

spring: 85- 95

Top of Page

NICKEL ALLOY 735

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: NICKEL SILVER 72 - 18

72% CU / 10% ZN / 18% NI

ASME SPEC NO.:

SAE ALLOY NO.:

MILITARY SPEC.:

ASTM ALLOY NO.:B122

FEDERAL SPECS: QCC 585

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.319

MOD. OF ELAST.(x 10****** PSI, tension): 18

ELECT. COND.(% IACS at 68 F (20 C) as annealed): 8

THERM. COND.

(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C): 21.5

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C): 9.0

Top of Page

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 50 - 68

15 - 60

1/2 hard: 63 - 75

49 - 69

full hard: 73 - 84

67 - 78

spring: 85 - 93

78 - 84

ELONGATION(% in 2 inches(= % in 50mm)

annealed: 11 - 37

1/2 hard: 3 - 16

full hard: 1 - 3

spring: 1 max.

ROCKWELL B HARDNESS
(.020 gauge and over (Rockwell F or 30 T where noted)

annealed: 81 - 100(F)

1/2 hard: 75 - 84

full hard: 83 - 88

spring: 89 - 92

Top of Page

NICKEL ALLOY 752

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: NICKEL SILVER 65 - 18

65% CU / 17% ZN / 18% NI

ASME SPEC NO.:

SAE ALLOY NO.: CA752

MILITARY SPEC.:

ASTM ALLOY NO.:B122

FEDERAL SPECS: QCC 585

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.316

MOD. OF ELAST.(x 10****** PSI, tension): 18

ELECT. COND.(% IACS at 68 F (20 C) as annealed): 6

THERM. COND.

(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C): 19

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C): 9.0

Top of Page

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 53 - 63

18 - 32

1/2 hard: 66 - 80

48 - 78

full hard: 78 - 91

75 - 90

spring: 90 - 101

88 - 99

ELONGATION(% in 2 inches(= % in 50mm)

annealed: 29 - 42

1/2 hard: 6 - 22

full hard: 3 - 7

spring: 1- 2

ROCKWELL B HARDNESS
(.020 gauge and over(Rockwell F or 30 T where noted)

annealed: 81 - 100(F)

1/2 hard: 68 - 82

full hard: 80 - 90

spring: 89 - 96

Top of Page

NICKEL ALLOY 762

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: NICKEL SILVER 59 - 12

59% CU / 29% ZN / 12% NI

ASME SPEC NO.:

SAE ALLOY NO.:

MILITARY SPEC.:

ASTM ALLOY NO.:B122

FEDERAL SPECS: QCC 585

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.310

MOD. OF ELAST.(x 10****** PSI, tension): 18

ELECT. COND.(% IACS at 68 F (20 C) as annealed): 9

THERM. COND.

(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C): 24

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C): 9.0

Top of Page

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 57 - 75

21 - 51

1/2 hard: 75 - 91

58 - 82

full hard: 90 - 105

82 - 97

spring: 109 - 122

101 - 110

ELONGATION(% in 2 inches(= % in 50mm)

annealed: 32 - 49

1/2 hard: 6 - 30

full hard: 3 - 6

spring: 1 max.

ROCKWELL B HARDNESS
(.020 gauge and over(Rockwell F or 30 T where noted)

annealed: 81 - 100(F)

1/2 hard: 77 - 98

full hard: 90 - 95

spring: 97 - 100

Top of Page

NICKEL ALLOY 770

NOMINAL DATA SHEET

CHEMICAL COMPOSITION: NICKEL SILVER 55 - 18

55% CU / 27% ZN / 18% NI

ASME SPEC NO.:

SAE ALLOY NO.: CA770

MILITARY SPEC.:

ASTM ALLOY NO.:B122

FEDERAL SPECS: QCC 585

DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.314

MOD. OF ELAST.(x 10****** PSI, tension): 18

ELECT. COND.(% IACS at 68 F (20 C) as annealed): 5.5

THERM. COND.

(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C): 17

COEFF.OF TH.EXPN.(Inches/inch/ F x 10(-******) from 68 F to 572 F (20 C to 300 C): 9.3

Top of Page

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)

(x 1000 PSI (MPA = KSI x 6.8948)

annealed: 61 - 76

23 - 41

1/2 hard: 78 - 95

64 - 93

full hard: 92 - 107

90 - 106

spring: 108 - 120

107 - 118

ELONGATION(% in 2 inches(= % in 50mm)

annealed: 39 - 48

1/2 hard: 5 - 24

full hard: 3 - 6

spring: 1 max.

ROCKWELL B HARDNESS
(.020 gauge and over(Rockwell F or 30 T where noted)

annealed: 81 - 100(F)

1/2 hard: 81 - 92

full hard: 90 - 96

spring: 97 - 100

Top of Page

AVAILABLE TEMPERS:
ANNEALED, 1/4 HARD, 1/2 HARD, 3/4 HARD, HARD, EX. HARD, SPRING, EX. SPRING

COIL/FOIL

.003
.004
.005
.010
.015
.020
.030
.040
.050
.062

WIRE form also available.

Top of Page

Disclaimer

Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.

Group Companies AircraftMaterialsUK.com

AVAILABLE TEMPERS: ANNEALED, 1/4 HARD, 1/2 HARD, 3/4 HARD, HARD, EX. HARD, SPRING, EX. SPRING

COIL/FOIL

AVAILABLE TEMPERS:
ANNEALED, 1/4 HARD, 1/2 HARD, 3/4 HARD, HARD, EX. HARD, SPRING, EX. SPRING